Cobertura SOLAR EVA
550mm Rollo 100M Cobertura SOLAR EVA
Valor $690 Dolares
| Item specifications |
(mm) Thickness |
(mm) Width |
(m/roll) Length |
| Z1261Extra fast curePID free | 0.45 | 550 | 100 |
550mm*100M SOLAR EVA FILM
|
Item |
Test method |
Unit |
Fast cure type |
|||
|
Z1261A |
Z1261 |
|||||
| Density |
ISO1183 |
g/cm³ |
0.95 |
0.95 |
||
| VA content |
TGA |
% |
26-33 |
26-33 |
||
| Softening point |
DSC |
°C |
55 |
55 |
||
| Surface hardness |
GB/T531-1999 |
Shore A |
65 |
65 |
||
| Tensile strenghth |
ISO527-3 |
MPa |
20 |
20 |
||
| Elongation at Break |
% |
550 |
550 |
|||
| Strenghth of Extension |
MPa |
6 |
6 |
|||
| UV cutoff wavelength |
UV-vis |
Nm |
— |
360 |
||
| Light transmittance |
GB2410-80 |
% |
91 |
90 |
||
| UV cutoff wavelength |
ISO489 |
— |
1.480 |
1.482 |
||
| (0.45MM; 120°C, 3mn)Thermal shrinkage |
Q/ZX001-2012 |
MD% |
≤3.0 |
≤3.0 |
||
|
TD% |
≤1.0 |
≤1.0 |
||||
| (14°C, 17min)Cross-linking degree |
Q/ZX001-2012 |
% |
≥75.0 |
|||
| Peeling strength | With Glass |
Q/ZX001-2012 |
N/cm |
>60 |
||
| With TPT |
N/cm |
>40 |
||||
| (90°C,90%RH, 1500hrs)Damp Heatresistance | Yellowness index |
Q/ZX001-2012 |
YI |
<3 |
||
| Peeling strenghth with glass |
N/cm |
>40 |
||||
| (Xenon lamp, 1500hrs)UV Exposureresistance | Yellowness index |
Q/ZX001-2012 |
YI |
<3 |
||
| Peeling strenghth with glass |
N/cm |
>40 |
||||
| Volume resistivity |
GB/T 1410 |
Ω·cm |
≥1*1015 |
|||
| Dielectric strength |
GB/T1408.1 |
Kv/mm |
>28 |
|||
| (60°C,85%RH,-1000V,96H)Power changes after PID test |
IEC61730-2:2004 IEC61215:2005 |
% |
<5% |
|||